EDTA滴定法测定再生锌原料中的锌含量
范丽新,汤淑芳
(北矿检测技术有限公司,北矿检测技术有限公司)
Determination of zinc content in regenerated zinc material by EDTA
FAN Lixin and TANG Shufang
(MTC Testing Technical CO.,LTD.,MTC Testing Technical CO.,LTD.)
摘要
图/表
参考文献
相似文献
本文已被:浏览 368次   下载 79
投稿时间:2018-08-11    修订日期:2019-01-20
中文摘要: 采用氟化铵-盐酸-硝酸-硫酸分解,氨水沉淀分离铁、锰、铅等共存元素,滤液中加入掩蔽剂掩蔽少量干扰元素,在pH 5~6的乙酸-乙酸钠缓冲溶液中,以二甲酚橙为指示剂,用EDTA标准滴定溶液滴定。测得结果为锌、镉合量,扣除镉量,即为锌量。试验方法用于测定再生新原料中锌,结果的相对标准偏差(RSD,n=11)为0.15%~1.03%。按照实验方法对分银渣样品进行加标回收试验,回收率为99.1%~101.6%。能满足日常对再生锌原料中锌含量的检测要求。
中文关键词: 滴定法  再生锌原料  
Abstract:The new determination method of zinc in regenerated raw material is established. Sample is decomposed by ammonium fluoride-hydrochloric acid-nitric acid-sulfuric acid, and the coexisting elements such as iron, manganese and lead are separated by ammonia water precipitation. A small amount of interfering elements were masked by adding a masking agent to the filtrate, and the zinc in the filtrate was titrated with EDTA standard titration solution in an acetic acid-sodium acetate buffer solution of pH 5-6, using xylenol orange as an indicator. The measured results combined with the amount of zinc and cadmium, and the amount of zinc is obtained by deduction the amount of cadmium. The relative standard deviations(RSD, n=11) of determination result were between 0.15% and 1.03%.The recoveries in samples of silver slag were between 99.1% and 101.6%.This method could meet the requirements of daily analysis of zinc content in regenerated zinc material.
文章编号:     中图分类号:    文献标志码:
基金项目:国家重大科学仪器设备开发专项工业过程在线分析检测仪器开发与应用(2016YFF0102500)
引用文本:
范丽新,汤淑芳.EDTA滴定法测定再生锌原料中的锌含量[J].中国无机分析化学,2019,9(1):47-53.
FAN Lixin,TANG Shufang.Determination of zinc content in regenerated zinc material by EDTA[J].Chinese Journal of Inorganic Analytical Chemistry,2019,9(1):47-53.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
86-10-63299759

杂志信息

期刊简介

相关下载

联系我们

电话:010-63299759

传真:010-63299754

QQ:XXXXXXX

Email:zgwjfxhx@163.com

邮编:100160

地址:北京市南四环西路188号总部基地十八区23号楼

关注微信公众号